RESUMEN
Single-wall nanotubes of isostructural AsPS4-xSex (x = 0, 1) are grown from solid-state reaction of stoichiometric amounts of the elements. The structure of AsPS4 was determined using single-crystal X-ray diffraction and refined in space group P1¯. The infinite, single-walled AsPS4 nanotubes have an outer diameter of ≈1.1 nm and are built of corner-sharing PS4 tetrahedra and AsS3 trigonal pyramids. Each nanotube is nearly hexagonal, but the ≈3.4 Å distance between S atoms on adjacent nanotubes allows them to easily slide past one another, resulting in the loss of long-range order. Substituting S with Se disrupted the crystallization of the nanotubes, resulting in amorphous products that precluded the determination of the structure for AsPS3Se. 31P solid-state NMR spectroscopy indicated a single unique tetrahedral P environment in AsPS4 and five different P environments all with different degrees of Se substitution in AsPS3Se. Optical absorption spectroscopy revealed an energy band gap of 2.7 to 2.4 eV for AsPS4 and AsPS3Se, respectively. Individual AsPS4 microfibers showed a bulk conductivity of 3.2 × 10-6 S/cm and a negative photoconductivity effect under the illumination of light (3.06 eV) in ambient conditions. Thus, intrinsic conductivity originates from hopping through empty trap states along the length of the AsPS4 nanotubes.